ASTM B163 Incoloy 800H(UNS N08810)Seamless Tube

Short Description:

ASTM B163 Incoloy 800H(UNS N08810) Seamless Tube for use in condenser and heat-exchanger service.Manufacture:Seamless process ,annealed

Product Detail

Product Tags

ASTM B163 Incoloy 800H(UNS N08810)Seamless Tube
 
Standard: ASTM B163
Specification for Seamless Nickel and Nickel Alloy Condenser and Heat-Exchanger Tubes
ASTM B163 Incoloy 800H(UNS N08810) Seamless Tube for use in condenser and heat-exchanger service.
 
 
ASTM B163 Incoloy 800H(UNS N08810) Seamless Tube Quick Details
Manufacture:Seamless process ,annealed
Wall thickness(WT): 1.24 mm-40.49 mm.
Outer diameter (OD): 10.3 mm-426 mm
Delivery Condition:Pickled&Annealed, Polished, Bright Annealed.
Length: 6M or specified length as required.
Ends: Plain End, Beveled End, Treaded
 
Additional Info
Port of Shipment: Any Port, China
Payment Terms: T / T, LC
Delivery: 25 days after payment
Surface: Tubes will be varnished to prevent rust.
Marking: Standard + Steel Grade + Size + Heat No + Lot No
Package: Bundles (hexagonal),Wooden Boxes,Crates (steel/wooden) or as required
 
 
Manufacture
The Tubes are made by the seamless process and The Tube will be furnished in the alloys and conditions as shown in Table 1.

TABLE 1 Alloy and Conditions
Alloy Condition
Nickel-iron-chromium alloyUNS N08810 annealed
 
 
Chemical Composition of ASTM B163 Incoloy 800H(UNS N08810)
The material shall conform to the composition limits specified in Table 2.

TABLE 2 Chemical Requirements
  Composition,%
  N08810
Nicke 30.0–35.0
Copper 0.75
Molybdenum ...
Iron 39.5 min B
Manganese 1.5
Carbon 0.05–0.10
Silicon 1.0
Sulfur 0.015
Chromium 19.0–23.0
Aluminum 0.15–0.60
Titanium 0.15–0.60
Phosphorus ...
Cerium ...
Zirconium ...
Yttrium ...
Boron ...
Cobalt ...
Columbium(Nb) ...
Tungsten ...
Nitrogen ...
B Element shall be determined arithmetically by difference.
 
 
Mechanical Properties and Other Requirements of of ASTM B163 Incoloy 800H(UNS N08810)
Mechanical Properties—The material shall conform to the mechanical properties specified in Table 3.

TABLE 3 Mechanical Properties of Tubes
Material and Condition Tensile Strength,
min, ksi (MPa)
Yield Strength
(0.2 % Offset),
min, ksi (MPa)
Elongation in 2in.or 50 mm(or 4 D)min, % Rockwell Hardness
(or equivalent) for
annealed ends A
Nickel-iron-chromium alloys:Annealed alloy UNS N08810 65 (448) 25 (172) 30 ...
 
Note: Rockwell or equivalent hardness values apply only to the annealed ends of stress-relieved tubing. Caution should be observed in using the Rockwell test on thin material,as the results may be affected by the thickness of specimen. For thickness under 0.050 in. (1.27 mm) the use of the Rockwell superficial or the Vickers hardness test is suggested. For hardness conversions for nickel and high-nickel alloys see Hardness Conversion Tables E140.
 
In the case of stress-relieved tubes furnished with annealed ends, the tension test shall be made on the stressrelieved tubes prior to annealing the ends.
 

Testings
Chemical Analysis
Mechanical Properties
Grain Size—A transverse sample representing full-wall thickness of annealed alloys UNS N08810  shall conform to an average grain size of ASTM No. 5 or coarser.
Hardness test—When annealed ends are specified for tubing in the stress-relieved condition (see Table 3), the hardness of the ends after annealing shall not exceed the values specified in Table 3.
 
Flare test—A flare test shall be made on one end of 1 % of the number offinished tube lengths from each lot.
The flare test shall consist of flaring a test specimen with an expanding tool having an included angle of 60° until the specified outside diameter has been increased by 30 %. The flared specimen shall not exhibit cracking through the wall.
 
Hydrostatic or Nondestructive Electric Test—Each tube shall be subjected to either the hydrostatic test or the nonde-structive electric test. The type of test to be used shall be at the option of the manufacturer, unless otherwise specified in the purchase order.
 
Hydrostatic Test:
Each tube with an outside diameter 1 ⁄ 8in. (3.2 mm) and larger and tubes with wall thickness of0.015 in. (0.38 mm) and over shall be tested by the manufacturer to an internal hydrostatic pressure of 1000 psi (6.9 MPa) provided that the fiber stress calculated in accordance with the following equation does not exceed the allowable fiber stress, S, indicated below. The tube shall show no evidence of leakage.

where:
P = hydrostatic test pressure, psi (MPa),
S = allowable fiber stress for material in the condition furnished, as follows:

  psi MPa
Annealed nickel-iron-chromium alloy UNS N08810 16 600 114.4
t = minimum wall thickness, in. (mm); equal to the specified average wall minus the permissible “minus” wall tolerance, Table 4 and Table X2.2, or the specified minimum wall thickness, and
D = outside diameter of the tube, in. (mm).
When stress-relieved tubes with annealed ends are to be tested hydrostatically, such pressure testing shall be done prior to annealing of the ends of the tube.



Dimensions and Permissible Variations
Outside Diameter and Wall Thickness—The permissible variations in the outside diameter and wall thickness of tube shall not exceed those prescribed in Table 4  as applicable. (See also Table 5 and Table 6.)
 
TABLE 4 Permissible Variations in Outside Diameter and Wall Thickness of Condenser and Heat Exchanger Tubes
 
N OTE 1—The tolerances in the table apply to individual measurements of outside diameter and include out-of-roundness (ovality), and apply to all materials and all conditions, except that for thin wall tubes having a nominal wall of 3 % or less of the outside diameter, the mean outside diameter shall comply with the permissible variations of the above table and individual measurements (including ovality) shall conform to the plus and minus values of the table with the values increased by 1 ⁄ 2 % of the nominal outside diameter.
 
N OTE 2—Eccentricity—The variation in wall thickness in any one cross section of any one tube shall not exceed plus or minus 10 % of the actual (measured) average wall of that section. The actual average wall is defined as the average of the thickest and thinnest wall of that section.
 

Material  Nominal Outside Diameter, in. (mm) Permissible Variations A
Outside Diameter, in. (mm  Wall Thickness,%   
+ Average Wall Minimum Wall
+ - + -
UNS N02200, UNS N02201,
and UNS N04400
1 ⁄ 2 to 5 ⁄ 8 (12.7 to 15.9), excl 0.005 (0.13) 0 12.5 12.5 25.0 0
5 ⁄ 8 to 1 1 ⁄ 2 (15.9 to 38.1), incl 0.005 (0.13) 0.005 (0.13) 10.0 10.0 20.0 0
over 1 1 ⁄ 2 to 3 (38.1 to 76.2), incl 0.010 (0.25) 0.010 (0.25) 10.0 10.0 22.0 0
UNS N06600, UNS N06601, UNS N06690,UNS N06045, UNS N06025, UNS
N06603, UNS N06696, UNS N08800,
UNS N06699
UNS N08810, UNS N08811, UNS
N08801,
UNS N08935
UNS N08825, UNS N06845, and UNS
N08120
UNS N06686
1 ⁄ 2 to 5 ⁄ 8 (12.7 to 15.9), excl 0.005 (0.13) 0.005 (0.13) 12.5 12.5 25.0 0
5 ⁄ 8 to 1 1 ⁄ 2 (15.9 to 38.1), incl 0.0075 (0.19) 0.0075 (0.19) 10.0 10.0 20.0 0
over 1 1 ⁄ 2 to 3 (38.1 to 76.2), incl 0.010 (0.25) 0.010 (0.25) 10.0 10.0 22.0 0
 
A Wall variations as indicated above are applicable only to the wall as ordered, for instance, to minimum or to average wall, but not to both.
 

TABLE 5 Alloy, A Condition, Tube Size, and Bend Radii Limitations
Tube OD, in. (mm) Average Tube Wall, in. (mm)B Minimum Bend Radius, in.(mm) 
Annealed
Condition
Stress-Relieved
Condition
Up to 1 ⁄ 2 (12.7), incl 0.046 to 0.057 (1.17 to 1.45), incl 1 3 ⁄ 1 6 (30.2) 1 1 ⁄ 4 (31.8)
Up to 1 ⁄ 2 (12.7), incl Over 0.057 to 0.120 (1.45 to 3.05), incl 1 (25.4) 1 1 ⁄ 8 (28.6)
Over 1 ⁄ 2 to 5 ⁄ 8 (12.7 to 15.9), incl 0.037 to 0.057 (0.94 to 1.45), incl 1 3 ⁄ 1 6 (30.2) 1 1 ⁄ 4 (31.8)
Over 1 ⁄ 2 to 5 ⁄ 8 (12.7 to 15.9), incl Over 0.057 to 0.120 (1.45 to 3.05), incl 1 (25.4) 1 3 ⁄ 1 6 (30.2)
Over 5 ⁄ 8 to 3 ⁄ 4 (15.9 to 19.0), incl 0.049 to 0.057 (1.24 to 1.45), incl 1 1 ⁄ 4 (31.8) 1 1 ⁄ 2 (38.1)
Over 5 ⁄ 8 to 3 ⁄ 4 (15.9 to 19.0), incl Over 0.057 to 0.109 (1.45 to 2.77), incl 1 3 ⁄ 1 6 (30.2) 1 1 ⁄ 4 (31.8)
Over 3 ⁄ 4 to 1 (19.0 to 25.4), incl 0.049 to 0.058 (1.24 to 1.47), incl 2 (50.8) 4 (101.6)
Over 3 ⁄ 4 to 1 (19.0 to 25.4), incl Over 0.058 to 0.109 (1.47 to 2.77), incl 1 3 ⁄ 4 (44.5) 2 1 ⁄ 4 (57.2)
A Applies for all alloys except alloy UNS N08810, alloy UNS N08801, and UNS N08811.
B To determine the bend radius applicable to minimum wall tubing,compute the corresponding average wall from the wall tolerances in Table 4, then use Table 5.
 

TABLE 6 Alloys, Size Ranges, and Yield Strength for Higher Yield Strength Tubes
Alloys Size Range, in. (mm) 0.2 % Yield Strength, ksi (MPa)
OD Wall Thickness Minimum Maximum
Nickel-chromium-iron Alloy UNS N06600 1 ⁄ 4 to 7 ⁄ 8 (6.35 to 22.23) Up to 0.100 (2.54) 40 (276) 65 (448)
Nickel-chromium-iron Alloy UNS N06601 1 ⁄ 4 to 7 ⁄ 8 (6.35 to 22.23) Up to 0.100 (2.54) 40 (276) 65 (449)
Nickel-iron-chromium Alloy UNS N08800 1 ⁄ 4 to 7 ⁄ 8 (6.35 to 22.23) Up to 0.100 (2.54) 40 (276) 65 (448)
Nickel-chromium-iron Alloy UNS N06690 1 ⁄ 4 to 7 ⁄ 8 (6.35 to 22.23) Up to 0.100 (2.54) 40 (276) 65 (448)
 
 
Length—When tube is ordered cut-to-length, the length shall not be less than that specified, but a variation of plus 1 ⁄ 8 in. (3.2 mm) will be permitted, except that for lengths over 30 ft (9.1 m), a variation ofplus 1 ⁄ 4 in. (6.4 mm) will be permitted.
Straightness—Material shall be reasonably straight and free of bends or kinks.
 

Workmanship, Finish, and Appearance
The material shall be uniform in quality and temper,smooth, commercially straight, and free of injurious imperfections.
 
 
Certification
When specified in the purchase order or contract, a report of the test results will be furnished.

Note:
All tubes shall be supplied as per applicable ASTM B163 /B163M Specification
Mill test certificates will be issued
We can provide 3.2 Certification according to the needs of you


Products categories

  • field:title/]

    ASTM B163 Incoloy 825(UNS N08

  • field:title/]

    ASTM B163 Incoloy 800HT(UNS N

  • field:title/]

    ASTM B163 Incoloy 800(UNS N0880

  • field:title/]

    ASTM B163 Incoloy 800H(UNS N0

  • field:title/]

    ASTM B163 Inconel 690(UNS N06

  • field:title/]

    ASTM B163 Inconel 601(UNS N06

  • field:title/]

    ASTM B163 Inconel 600 (UNS N066

  • field:title/]

    ASTM B163 Monel 400(UNS N04400)